Your application - our solution: Find out more about the perfect sample preparation in the field of metallurgy. Read our application reports with tips about comminution or take a look in our practical grinding report data base with numerous sample grindings with detailed information.
| Material | Feed size | Final fineness | No. | |
| Alloy | 1 - 2 mm | <100µm | M0098003 | details |
| aluminium - foil | | <250µm | M002113 | details | |
| aluminium splinters | < app. 30x1mm* | fineness was reached | M002135 | details |
| cast iron | 10x5mm | approx. 100µm | M0097047 | details |
| Cerium oxide/copper oxide (90%/10%) | app. <30µm | sticks heavily!*2 | M002128 | details |
| Copper (resin, sample A) | < 2cm | < 0,25mm | M0097268 | details |
| copper ore | * | < 110µm * | M0099025 | details |
| copper ore | 150µm | 57% < 50µm * | M0098346 | details |
| Fe,Sn,Cu ...-compounds: Cu2O (1), Cu2S (2), SnS (3), FeS2 (4) | 10-100µm | d90 <0,4µm | M090024 | details |
| Ferro tungsten | 2cm | ca. 95%<120µm | M001182 | details |
| Ferro tungsten (75%) | app.2,5cm | approx. 6-8mm | M003102 | details |
| Ferro vanadium | < 8mm | ~ < 300µm | M0097222 | details |
| Ferro vanadium | < 1cm | ~ 300-500µm | M0097144 | details |
| Ferro vanadium | | app. 1mm / app.74%<50µm | M003253 | details | |
| Ferrochrome | < 8mm | 67%< 200µm 93% < 200µm | M0098206 | details |
| Ferrochrome | 4 - 5cm | < 1 - 2cm | M0098195 | details |
| Ferrochrome | 3-4mm | 15% <160µm / 51% < 160µm / 80% <160µm | M004028 | details |
| Ferrochrome | <60mm *1 | < app.30mm | M003042 | details |
| ferrosite | 3cm | 36% < 90µm | M0098385 | details |
| Ferrotitanium (70% titanium) | < 6cm | < ca. 100µm | M0098096 | details |
| Ferrum oxide/chrome oxide | d50 < 8,4µm | d90< 2,4µm / d90< 1,9µm d90< 1,3µm / d90< 1,2µm | M004054-1 | details |
| gold dust | <120µm | flocculating | M002146 | details |
| Hard metal (sintered, WC) | app.<2-3cm | 120-130µm | M0099015 | details |
| hardmetal | 3,5 cm | 5,3% > 180µm 21,5% < 100µm | M0098253 | details |
| Iron (pellets) | <1cm | 100%<75µm 50%<19,6µm | M001156 | details |
| iron ore | 5x5x5mm | 16,86 % > 140 µm | M0098247 | details |
| Iron powder | <60mm*1 | < 1-1,5cm | M002053 | details |
| Iron silicide strips | 8cm | < 0,25mm | M0097249 | details |
| iron slag | 5 x 3cm | approx. 14mm | M0098135 | details |
| Metal (brittle) | < 2cm | 80% < 500µm | M0098186 | details |
| Ore | <5-6cm | < ca. 150µm | M003058 | details |
| Ore sample | <6-8mm | ~96%< 1,12mm*2 | M004136 | details |
| sample A sintered alloy of Ti-Fe-Ni | < 10mm | output:4,35g sieving: 10%<100µm | M002139 | details |
| slag with copper | 3 cm | < 1,5 mm | M0097115 | details |
| slag/Cu-metal | | homogenes Pulver | M003073 | details | |
| Stainless steel (powder) | 70µm | ca. 100µm / ca. 300µm* / 150µm (build flakes) | M0097090 | details |
| Steel granulate | <5-7mm | < ca. 0,5-1mm | M002105 | details |
| Steel turning chips | 40x2mm, 0,1mm thick | <800µm | M070536 | details |
| TiSi2 | powder | d50 <0,5µm | M080288 | details |
| TiSi2, Titansilicid | powder | M090049 | details | |
| Titansilicid | << 1mm | << 1mm | M090115 | details |
| tungsten(VI)oxide WO3 | d90 <22µm*1 | d50 <0,46µm*3 d95<1,0µm | M002245 | details |
| Wolfram-Rhenium | 3 - 4mm | 49.6% > 160µm 37.1% = 63-160µm | M0098115 | details |
| Wolfram/tungsten | 1cm | app. 200-300µm | M0096450 | details |